Influence of nitrogen ion implantation on the nanostructure and corrosivity of Ni/stainless steel substrates


Journal: Vol.9, No.2, Spring 2016 - Article 2   Pages :  77 Until 83



Article Code:
PCCC-2015-12-21-308

Authors:
A.R. Grayeli Korpi: Nuclear Sciences and Technology Research Institute - Physics and Accelerators School
Kh. M. Bahmanpour: Science & Research Branch, Islamic Azad University - Plasma Physics Research Center


Article's abstract:

Ion implantation is a surface modification technology to produce new material on the surface by impingement of high energy ions from the ion accelerator. In this work, AISI 304 stainless steels were coated with 90 nm Ni film by electron beam deposition and implanted by a flow of 5×1017 N cm−2 at 400 K temperature with different implantation energies of 10, 20, 30 and 40 keV. The prepared samples were corrosion tested in 3.5 NaCl solution using potentiodynamic polarization technique. Crystallographic and morphological structure of the samples were analyzed by Xray diffraction XRD and scanning electron microscope SEM respectively. A clear correlation between the physical analyses XRD and SEM and the potentiodynamic results is achieved. The highest corrosion resistance with a corrosion current density of 0.172 µA cm2 was achieved in case of sample which was N ion implanted at 20 keV energy.


Keywords:
Ni thin films; Corrosion; Potentiodynamic; Stainless steel; SEM

References:
[1] N. Mottu, M. Vayer, J. Dudognon, R. Erre, Surf. Coat. Technol., 200 (2005) 262131-2136. [2] H.-P. Feng, C.-H. Hsu, J.-K. Lu, Y.-H. Shy, Mater. Sci. Eng. A, 347 (2003) 123-129. [3] P. Misaelides , F. Noli , J. P. Riviere , J. Delafond, Meth. Phys. Res. Sect. B., 129 (1997) 221-227. [4] A. Neville , F. Reza , S. Chiovelli , T. Revega, Wear, 259 (2005) 181-195. [5] P. Saravanan, V. S. Raja , S. Mukherjee, Surf. Coat. Technol., 201 (2007) 8131-8135. [6] M. Oikawa, T. Kamiya, M. Fukuda, Nucl. Instr. Meth., B210 (2003)54-58. [7] Ph. Moretto, C. Michelet, A. Balana, Nucl. Instr. Meth., B181 (2001)104–109. [8] X.F. Wang, L.Y. Chen, Z.W. Hu, X.H. Wang, J. Zhang, J. Li,L.J. Wu, S.H. Wang, Z.L., Chin. Phys. Lett., 21 (2004)821–824. [9]. N. Mottu, M. Vayer, J. Dudognon, R. Erre, Surf. Coat. Technol, 200 262131-2136, 2005. [10] Y. Fu, X. Wu, H. En-Hou, W. Ke, K. Yang, Z. Jiang, Electrochim. Acta, 54 4005-4014, 2009. [11] C. Garcia, F. Martin, Y. Blanco, M. P. de Tiedra, M. L. Aparicio, Corros. Sci, 51 76-86, 2009. [12] R. W. Revie, H. H. Uhlig, corrosion and corrosion control, Wiley interscience, p 407 2008,. [13] L. Pranevicius, Surf. Coat. Technol. 158 99–104, 2002 [14] B. Chico, L. Martinez, F.J. Perez, Appl. Surf. Sci, 243 409–414, 2005 [15] R. F. A. Jargelius-Pettersso, Corros. Sci, 41, 1639-1664 1999. [16] S. Fujimoto, H. Hayashida, T. Shibata, Mat. Sci. Eng. A267 314–318 1999. [17] V. Singh, K. Marchev, C.V. Cooper, E.I. Meletis, Surf. Coat. Tech, 160 249–258 2002. [18] A.R. Grayeli-Korpi, H. Savaloni, App. Surf. Sci. 258 (2012) 9982-9988. [19] H. Savaloni, M. Habibi, App. Surf. Sci. 258 (2011) 103-112. [20] F. Seidel, H. R. Stock, P. Mayer, Surf. Coat. Technol., 108 (1998) 271-275. [21] C.-O. A. Olsson, Corros. Sci., 37 (1995) 467-479.


Article's file
Page view: 1771
Article's download quantity : 25


Article System Login
Introduction

Manager-in-Chief:
Prof. Zahra Ranjbar
Editor-in-Chief:
Dr. Farahnaz Nourmohammadian
Assistant Editor:
Dr. Mozhgan Hosseinnezhad
ISSN:
2008-2134
ISSN (online):
2383-1790
Publisher:
Institute for Color Science and Technology (ICST)

Quick Access
Publications
E-Vote
What is your opinion about the manuscript subscription system of PCCC website?
Excellent
Good
Fair
Poor
Website Statistics
Page view:1,772
Online Visitors:25