Acrylic resin derivatives as modifier for potassium silicate binder in zinc-rich coatings: electrochemical studies


Journal: Vol.7, No.3, 2014 - Article 7   Pages :   Until 



Article Code:
PCCC-02-08-2013-248

Authors:
Iman Mirzaie Goodarzi: Petroleum University of Technology - Abadan Faculty of Petroleum Engineering
Mansour Farzam: Petroleum University of Technology - Abadan Faculty of Petroleum Engineering
M. R. Shishesaz: Petroleum University of Technology - Abadan Faculty of Petroleum Engineering
Daavood Zaarei: South Tehran Branch, Islamic Azad University - Technical Faculty


Article's abstract:

Water based inorganic alkali silicate binder of zinc rich primer was modified by adding acrylic resin derivatives. Several series of primer coatings were formulated by adding 5, 10 and 15 wt of acrylic and acrylic/styrene copolymer to potassium silicate binder and used as binder in zinc rich coatings. The formulated primers were applied on low carbon steel plates and the corrosion protection properties of these primers were evaluated by electrochemical impedance spectroscopy EIS, corrosion potential measurements, salt fog test and scanning electron microscope SEM. The results indicated that the addition of 5 acrylic/styrene copolymer and/or 10 acrylic resin into the inorganic silicate binder led to improvement of corrosion protection performance of formulated primers.


Keywords:
inorganic silicate binders; acrylic/styrene copolymer; Salt fog; SEM.

References:
1. H. H. Chua, B. V. Johnson, T. K. Ross, The protection of mild steel by zinc-rich paint in flowing aerated 0.5 M NaCl solutions, Corros. Sci., 18(1978), 505-510.#2. A. Gergely, É. Pfeifer, I. Bertóti, T. Török, E. Kálmán, Corrosion protection of cold-rolled steel by zinc-rich epoxy paint coatings, Corros. Sci., 53(2011), 3486-3499.#3. N. Hammouda, H. Chadli, G. Guillemot, K. Belmokre, The corrosion protection behaviour of zincrich epoxy paint in 3% nacl solution, Adv. Chem. Eng. Sci., 1(2011), 51-60.#4. T. Morizane, Y. Yamada, J. Takagishi, H. Matsuno, M. Ohshiba, Aqueous inorganic zinc-rich coating composition, US Pat. 0030584, 2011.#5. G. Canosa, P. V. Alfieri, C. A. Giudice, Environmentally friendly, nano lithium silicate anticorrosive coatings, Prog. Org. Coat., 73(2012), 178-185.#6. M. N. Kakaei, I. Danaee, D. Zaarei, Investigation of corrosion protection afforded by inorganic anticorrosive coatings comprising micaceous iron oxide and zinc dust, Corros. Eng., Sci. Technol., 48(2012), 194-198.#7. C. A.Gervasi, A. R. DI. Sarli, E. Cavalcanti, O. Ferraz, E. C. Bucharsky, S. G. Real, J. R. Vilche, The corrosion protection of steel in sea water using zinc-rich alkyd paints. an assessment of the pigment-content effect by eis, Corros. Sci., 36(1994), 1963-1972.#8. R. Pedram, T. K. Ross, The protection of mild steel by zinc-rich paint in flowing aerated 0.5 M NaCl solution—III: The effect of zinc content, Corros. Sci., 18(1978), 519-522.#9. S. Shreepathia, P. Bajajb, B. P. Mallika. Electrochemical impedance spectroscopy investigations of epoxy zinc rich coatings role of Zn content on corrosion protection mechanism, Electrochim Acta, 55(2010), 5129-5134.#10. C. M Abreu, M. Izquierw, M. Keddam, X. R. Novo, H. Takenouti, Electrochemical behaviour of zinc-rich epoxy paints in 3% NaCl solution, Electrochim Acta, 41(1996), 2405-2415.#11. O. O. Knudsen, U. Steinsmo, M. Bjordal, Zinc-rich primers—test performance and electrochemical properties, Prog. Org. Coat., 54(2005), 224-229.#12. M. O’Donoghue, R. Garrett, V. J. Datta, S. Osborne, P. Roberts, Fast production schedules with novel zinc primers and polyaspartic ester topcoats, JPCL, (2005).#13. W. E. Kemp, Sacrificial anode coating, US Pat. 3231535, 1966. 14. G. H. Davies, P. A. Jackson, Primer coating of steel, US Pat. 8128996, 2012.#15. R. W. Beers, J. Lakritz, Zinc enriched lithium silicate-latex coating composition, US Pat. 3884863, 1975.#16. J. Neel, B. Bonnel, Acrylo-silicate binders for coating compositions, US Pat. 3450661, 1969.#17. L. Zhang, A. Ma, J. Jiang, D. Song, J. Chen, D. Yang, Anti-corrosion performance of waterborne Zn-rich coating with modified silicon-based vehicle and lamellar Zn (Al) pigments, Prog. Nat. Sci., 22(2012), 326-333.#18. M. Selvaraj, S. Guruviah, The electrochemical aspects of the influence of different binders on the corrosion protection afforded by zinc-rich paints, Surf. Coat. Int., 80(1997), 12-17.#19. S. F. Jr. M. Morcillo, S. Feliu. Deterioration of cathodic protection action of zinc-rich paint coatings in atmospheric exposure, Corrosion (Houston, TX, U. S.), 57(2001).#20. A. Kalendová, P. Kalenda, D. Veselý, Comparison of the efficiency of inorganic nonmetal pigments with zinc powder in anticorrosion paints, Prog. Org. Coat., 57(2006), 1-10.


Article's file
Page view: 3150
Article's download quantity : 467


Article System Login
Introduction

Manager-in-Chief:
Prof. Zahra Ranjbar
Editor-in-Chief:
Dr. Farahnaz Nourmohammadian
Assistant Editor:
Dr. Mozhgan Hosseinnezhad
ISSN:
2008-2134
ISSN (online):
2383-1790
Publisher:
Institute for Color Science and Technology (ICST)

Quick Access
Publications
E-Vote
What is your opinion about the manuscript subscription system of PCCC website?
Excellent
Good
Fair
Poor
Website Statistics
Page view:3,151
Online Visitors:27