Corrosion Behaviour of Nickel Coated AISI 316 Stainless Steel as a Function of Annealing Temperature

Journal: Vol.9, No.3, 2016 - Article 4   Pages :  173 Until 181

Article Code:

A.R. Grayeli Korpi: Nuclear Sciences and Technology Research Institute - Physics and Accelerators School

Article's abstract:

AISI 316 stainless steels were coated with 250 nm Ni film by electron beam deposition and post-annealed at different temperatures with a nitrogen flow of 600 cm3min-1 nitrogen. The prepared samples were corrosion tested in 1.0 M sulphuric acid solution using potentiodynamic technique. Crystallographic and morphological structure of the samples were analyzedanalysed by X-ray diffraction (XRD) and atomic force microscopy (AFM) respectively before corrosion test, and scanning electron microscope (SEM) after corrosion test. A clear correlation between the physical analyses (XRD, AFM and SEM) and the potentiodynamic results was is achieved. It is found that both surface roughness and the annealing temperature have important role on corrosion resistance performance of the samples produced in this work and the optimum results can be obtained at annealing temperature of 623 K for AISI 316 samples where both surface roughness and temperature (diffusion effect) have reached their critical values.

Ni thin films; Potentiodynamic; Stainless steel; Corrosion

1. J. G. Parr, A. Hanson, Stainless Steel, ASM International, Metals Park, OH, USA, 1986, 63-88. 2. A. I. M. Bernstin, Handbook of Stainless Steels, McGraw-Hill, New York, USA, 1977, 15.1-15.6. 3. R. M. Davison, T. DeBold, M. J. Johnson, Metals Handbook, ASM International, Metals Park, OH, USA, 1980, 550-565. 4. D. Stoychev , P. Stefanov , D. Nicolova , I. Valov, Ts. Marinova, Chemical composition and corrosion resistance of passive chromate films formed on stainless steels 316 L and 1.4801, Mater. Chem. Phys., 73(2002), 252-258. 5. A. Neville , F. Reza , S. Chiovelli , T. Revega, Corrosion and synergy in a WC Co CrWC Co Cr HVOF thermal spray coating-understanding their role in erosion–corrosion degradation, Wear, 259(2005), 181-195. 6. P. Saravanan, V. S. Raja , S. Mukherjee, Effect of plasma immersion ion implantation of nitrogen on the wear and corrosion behavior of 316LVM stainless steel, Surf. Coat. Technol,. 201(2007), 8131-8135. 7. A. R. Grayeli Korpi, Kh. M. Bahmanpour, Influence of nitrogen ion implantation on the structure and corrosion resistance of stainless steel substrates coated with Ni nanolayer, Prog. Color Colorants Coat., 9(2016), 77-83. 8. V. Vignal , N. Marya, P. Ponthiaux , F. Wenger, Influence of friction on the local mechanical and electrochemical behaviour of duplex stainless steels, Wear, 261(2006), 947-953. 9. C. Garcia, F. Martin , Y. Blanco, M. P. de Tiedra, M. L. Aparicio, Corrosion behaviour of duplex stainless steels sintered in nitrogen, Corros. Sci., 51(2009), 76-86. 10. J. H. Potgieter, P. A. Olubambi, L. Cornish, C. N. Machio, M. Sherif El-Sayed, Influence of nickel additions on the corrosion behaviour of low nitrogen 22% Cr series duplex stainless steels, Corros. Sci.,50(2008), 2572-2579. 11. H. Baba , T. Kodama, Y. Katada, Role of nitrogen on the corrosion behavior of austenitic stainless steels, Corros. Sci., 44(2002), 2393-2407. 12. B. R.Tzaneva, L. B. Fachikov and R. G. Raicheff, Pitting corrosion of Cr–Mn–N steel in sulfuricsulphuric acid media, J. Appl. Electrochem., 36(2006), 347-353. 13. Y. Fu, X. Wu, H. En-Hou, W. Ke, K.Yang,Z. Jiang, Effects of nitrogen on the passivation of nickel-free high nitrogen and manganese stainless steels in acidic chloride solutions Electrochim. Acta., 54(2009), 4005-4014. 14. R. Merello, F. J. Botana, J. Botella, M. V. Matres,M. Marcos, Influence of chemical composition on the pitting corrosion resistance of non-standard low-Ni high-Mn–N duplex stainless steels, Corros. Sci., 45(2003), 909-921. 15. C. M Tseng, H. Y Liou, W. T Tsai, The influence of nitrogen content on corrosion fatigue crack growth behavior of duplex stainless steel, J. Mater. Sci. Eng. A, 344(2003), 190-200. 16. J. W. Park, V. Shankar Rao, H. S. Kwon, Effects of Nitrogen on the RepassivationBehavior of Type 304L Stainless Steel in Chloride Solution, Corrosion., 60(2004), 1099-1103. 17. H. Y. Ha, H. S. Kwon, Effects of Cr2N on the pitting corrosion of high nitrogen stainless steels, Electrochim. Acta,. 52(2007) 2175-2180. 18. U. KamachiMudali, P. Shankar, S. Ningshen, R. K. Dayal,H. S. Khatak, B. Raj, On the pitting corrosion resistance of nitrogen alloyed cold worked austenitic stainless steels, Corros. Sci., 44(2002), 2183-2198. 19. H. Baba,Y. Katada, Effect of nitrogen on crevice corrosion in austenitic stainless steel, Corros. Sci., 48(2006), 2510-2524. 20. Y. X. Qiao, Y. G. Zheng, W. Ke, P. C. Okafor, Electrochemical behaviour of high nitrogen stainless steel in acidic solutions, Corros. Sci,. 51(2009), 979-986. 21. W. W. Mullins, The effect of thermal grooving on grain boundary motion, Acta metal., 6(1958), 414-427. 22. F. Maghazeii, H. Savaloni, M. Gholipour-Shahraki, The influence of growth parameters on the optical properties and morphology of UHV deposited Ni thin films, Optic Commun, 281(2008, 4687-4695 23. S. H. Kang, Y. S. Obeng, M. A. Decker, M. Oh, S. M. Merchant, S. K. Karthike, C. S. Seet, A. S. Oates, Effect of Annealing on the Surface Microstructural Evolution and the Electromigration Reliability of Electroplated Cu Films, J. Elect. Mater., 30(2001), 1506-1511. 24. M. Firouzi-Arani, H. Savaloni, M. Ghoranneviss, Dependence of surface nano-structural modifications of Ti implanted by N+ ions on temperature, Appl. Surf. Sci, 256(2010), 4502-4511 25. U. Schmid, The impact of thermal annealing and adhesion film thickness on the resistivity and the agglomeration behavior of titanium/platinum thin films, J. Appl. Phys., 103 (2008), 054902- 054902. 26. J. R. Davis, Stainless Steels ASM Specialty Handbook, ASM International, OH, USA, 1996, pp. 22-24. 27. D.E. Aspnes, E. Kinsbron, D. D. Bacon, Optical properties of Au: Sample effects, Phys. Rev. B: Condens. Matter Mater. Phys., 21(1980), 3290-3299. 28. H. Savaloni, M. Gholipour-Shahraki, Structural characteristics in UHV deposited Ti thin film, Nanotechnology, 15(2004), 311-319. 29. C.–O. A. Olsson, D. Landolt, Passive films on stainless steels-chemistry, structure and growth, Electrochim. Acta., 48(2003), 1093-1104.

Article's file
Page view: 1348
Article's download quantity : 20

Article System Login

Prof. Zahra Ranjbar
Dr. Farahnaz Nourmohammadian
Assistant Editor:
Dr. Mozhgan Hosseinnezhad
ISSN (online):
Institute for Color Science and Technology (ICST)

Quick Access
What is your opinion about the manuscript subscription system of PCCC website?
Website Statistics
Page view:1,349
Online Visitors:30